spring steel

E Steel Sdn Bhd are Asia Metal traders, high performance metal exporters, metal supply chain management , providing Alloy Steel, Nickel Alloy, Stainless Steel, Titanium to the wide arrays of engineering industries/sectors. Shall you have inquiry on Alloy steels, Stainless steels, Nickel Alloy & Titanium, please do not hesitate to inquiry @ https://www.esteelsuppliers.com/new/enquiry/

SKU: Case Hardening steel-2-1 Category: Tags: , ,


SUP9 Spring Steel | 55CrMnA | 55Cr3 | 1.7176 | 527A60 | 55C3 | ASTM 5155

JIS SUP9 Steel is a high quality Cold work Spring Steel, It belong to the high quality high carbon alloy Spring Steel. Oil Quenched & Tempered Hardness is 28-34 HRc. SUP9 steel Annealing delivery hardenss less than 250HB.


Chemical composition

C(%) 0.52-0.60 Si(%) 0.15-0.35 Mn(%) 0.65-0.95 P(%) ≤0.030
S(%) ≤0.035  Cr(%) 0.65-0.95

Equivalent Of SUP9 alloy Spring Steel

USA Germany China Japan France England Italy Poland ISO Austria Sweden Spain
5155 / G51550 55Cr3 / 1.7176 55CrMnA SUP9 55C3 ≈527A60 55Cr3

Heat treatment Related

  • Annealing of SUP9 Spring Steel

Slowly heated to 740-770 ℃ and allow enough times, let the steel to be thoroughly heated, Then cool slowly in the furnace. The SUP9 tool  steel will get MAX 250 HB (Brinell hardness).

  • Hardening of SUP9 Spring Steel

SUP9 steels should be heated uniformly to 830-860°C (1526-1580°F) until completely heated through. About 30 min per 25 mm of ruling section is to be provided and then the steels should be immediately quenched in oil.

  • Tempering of SUP9 Spring Steel

Tempering of SUP9 steels is performed at 460-510°C, Soak well at the selected temperature and soak for at least one hour per 25mm of total thickness.

 Mechanical Properties

The mechanical properties of SUP9 Spring Steels are outlined in the following table.

Tensile strength Conditions to yield strength Elongation Reduction of area Hardness (Hot Rolled) Hardness (Cold Drawn)
σb (MPa):≥1225(125) σ0.2 (MPa):≥1080(110) δ5 (%):≥9 ψ (%):≥20 ≤321HB;


SUP9 steels, Highlight the advantage is good hardenability, another hot working performance, comprehensive mechanical properties, Decarburization resistance is also good big cross section of various important spring, such as automobile, locomotive, large plate spring, spring, etc. SUP9 Spring main used for heavy vehicles, tractors, industrial production load, stress and the diameter of the larger plate spring and helical spring